The elevator makes high anticorrosion performance electrophoretic paint
Product Introduction :
HLS-1701ALB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below :
Have excellent corrosion resistance and weathering resistance, especially suitable for the bottom surface of a painting；
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
Good stability of bath can adaptable for a longer updating cycle.
Coating fullness of good, better substrate hiding .
Main ingredients :
| Pigmen:Titanium pigment, carbon black, kaolin, antirust pigment |
| Solvent::alcohol ether |
| Neutralizing agent :organic acid |
| Additives: surface active agent, prevent shrinkage cavity agent |
Filling tank proportion and method :
⑴ Bath preparation
Ratio:
Resin 1200.00
Paste 200.00
DI water 2000.00
Total 3400.00
⑵ Ripening conditions
Sample quantity: 3000～5000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-35℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(175-185)℃×(20-30)min (Keeping temperature of parts coated)
Construction equipment :
Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment:
| Electrophoresis tank | Circulation devices (including filter, fill the paint device) | DI water equipment |
| DC power supply and the power supply unit | Anode box (tube) and circulation device | Ultrafiltration device |
| Cleaning devices | Heat exchanging equipment | Curing device |
Customers in the elevator industry :